ảnh hưởng của SiO2 và Al2O3 tới độ bền ăn mòn hợp kim ZnNi trong môi trường tự nhiên và nhân tạo

Tóm tắt

Electrodeposited   zinc-nickel   alloy  coatings  (with  composition  of  Ni:  0,  7  and  14% by weight)  in  ammonic  bath  have  experimented  in  natural  atmospheres  and  artificial  atmospheres (salt-fog  test).  Results  in  salt-fog  test  show  that  corrosion  resistance  of  ZnNi  coatings  is  higher by  far  than  Zn  coating,  especially  ZnNi  14%  coating.  But,  results  in  natural  test  are  on  the contrary.   Coating   composition   with   Si02  and  AI2O3  inert   particles   has  effect   on   improve significantly  corrosion  resistance  of  these  electrodeposited  alloy  coatings.  Results  are  affirmed by tests  in natural  atmospheres  and artificial  atmospheres  (salt-fog  test).